• Şişecam Tinted Float Glass is the trademark of body tinted float glass range of Şişecam Flat Glass.
• Manufactured by adding coloring agents to the raw batch before melting process.
• Laminated glass, toughened glass, heat strengthened glass, enamalled glass, bent glass, coated glass, acid etched glass, sandblasted glass and mirror can be produced by applying secondary processes to Şişecam Tinted Float Glass;

Colors

Green, gray, bronze, blue, turquoise and dark gray colors are available.

Performance Table

“Daylight” and “Solar Energy” properties are calculated with “TNO Science and Industry - WIS 3.01” program using spectral measurements in compliance with EN 410.

“U-value” is calculated with “TNO Science and Industry - WIS 3.01” program according to EN 673. The emissivity measurements used for calculations are in compliance with EN 673 (Annex A) and EN 12898.

Thermal stresses or building codes may require the use of heat-treated glass. This document is not an evaluation of the risk of glass breakage from thermal stresses. Please contact Şişecam Flat Glass to ensure the correct form of glass to be supplied for the structure.

Specifications, technical and other data are based on information available at the time of preparation of this document and are subject to change without notice.

Şişecam Flat Glass can not be held responsible for any deviation between the data introduced and the conditions on site. This document is only informative, in no way it implies an acceptance of the order by Şişecam Flat Glass.

Daylight Transmittance (%): The ratio of the visible spectrum (light) that is transmitted through glass.

Daylight Reflectance (outdoor) (%): The ratio of the visible spectrum (light) that is reflected outside by glass.

Solar Factor: The percentage of total solar radiant heat energy entering. The room through the glass. The lower solar factor means better solar control.

Shading Coefficient: The ratio of solar factor of a particular glass type to the solar factor of 3 mm clear float glass, set in identical conditions. The lower shading coefficient means better solar control.

U value (W/m2K): A measure of the rate of heat loss of a building component. The lower U value means better heat control and more comfort in winter

Quality

Şişecam Tinted Float Glass range is manufactured in accordance with EN 572-2 Glass in Building- Basic Soda Lime Silicate Glass Products - Part 2: Float glass.

Storage

Glass packs or crates should be stored at an angle of 5o from the vertical. If bowing of the crates is observed, they should not be stored further and the row should be unpacked immediately.

Glass packs or crates should not be stored outside. They should be stored in a closed environment where appropriate temperature and humidity conditions are provided. Recommended values for storage: temperature between 9-25oC, humidity 70% . During the storage of the packs and the crates, contact with rain, snow or any kind of water should be avoided. High risk of corrosion should be considered when the glass panes get wet during storage. Therefore, if the glass panes get wet because of condensation or any other reason, they should be cleaned immediately before drying.

The loading or unloading of the packs from the stillages should be well balanced.

For the storage of the Jumbo packs, wooden wedges with rubber are recommended.

For the storage of the machine or split sizes, wooden or metal (with rubber) wedges are recommended.

Stillage and the wedges should be supported with rubber pieces in order to tolerate the level differences that are originating from the ground.

Wooden wedges should be made out of hornbeam or beech that are dried in an oven.

Glass packs, in which there are broken or cracked panes, must not be stored.

Washing

Hardness of the water to be used for washing the glass panes should be maximum 5o Fr and pH should be between 6-8. The electrical conductivity of the washing water is recommended as 1 µS/cm for the glasses to be coated off-line and less than 30 µS/cm for insulating glass units. Brushes of the washing machine should be soft in order to avoid scratches on the glass. The water on the glass should be removed with air knife before drying.

Carrying and Handling (in the plant)

Glass packs or crates should be carried at an angle of 5o from the vertical. (Never horizontal)

Outdoor transportations should be made with closed vehicles that are protected from dust and water.

There should not be any broken or cracked panes inside the glass packs. Broken or cracked panes have the risk to scratch the glasses by side, and may cause injury.

Glass packs should be stepped on rubber or pad floor. Direct contact with metal or wood should be avoided.

An appropriate interleaving material such as powder or paper should be used between the glass panes. Inappropriate material can cause scratches, cracks and corrosion. In case of paper used as interleaving material, the pH should be between 5,5-7 and it should not leave any ash when it is burned.

All interleaving material should be clean and dry.

Loading and carrying equipment should be undamaged.

Glass packs or crates should be fastened to the vehicle during transportation.

Loading or unloading of the glass packs or crates to the vehicle should be carried out with appropriate equipment. Inappropriate equipment can cause accidents and breakages of glass. Removing the packages of glass should be made with care.

Cutting

Cutting wheel, cutting oil and cutting pressure should be appropriated.

The glass should be snapped off immediately after cutting process is completed.

The surfaces of the cutting tables should be clean and smooth.

The glass that will be cut should have the same temperature all around. Glass that is exposed to sunshine may not be cut properly because of the temporary stresses.

If glasses are heat-treated above 480oC, cutting and breaking problems can occur due to the secondary processes.