Şişecam Solar Control Low-E Glass Neutral

Şişecam Solar Control Low-E Glass Neutral is Şişecam Flat Glass’ heat and solar control glass.

Advantages

The coating provides heat and solar control properties at the same time.
Decreases heating and cooling expenses.
Do not compromise on natural daylight and transparency.
Ensures maximum benefit from daylight.
Reduces condensation on glass surface.
Eliminates cold spots and hot spots close to windows.
Provides extremely high levels of protection against UV radiation over 75%, therefore helps to reduce fading and ageing effects.

Description

Şişecam Solar Control Low-E Glass Neutral is Şişecam Flat Glass’ heat and solar control glass.

Insulating Glass Unit (IGU) manufactured with Şişecam Solar Control Low-E Glass Neutral reduces heat loss from windows by 77% compared to single glazing, by 50% compared to ordinary IGU. Therefore effective heat insulation in winter is provided and heating expenses are reduced. It also decreases solar energy transmission by 40% compared to ordinary IGU. Therefore it keeps cooler in summer and cooling expenses are reduced.

Applications

Şişecam Solar Control Low-E Glass Neutral is preferred in residential, small/medium sized commercial buildings and provides comfortable living areas to end users with its thermal insulation and solar control property.

Neutral 62/44; is preferred in residential buildings, schools, small/medium-sized commercial buildings where thermal insulation and solar control are required.

Neutral 50/33; is preferred in residential buildings, schools, small/medium-sized commercial buildings where optimum daylight transmission and efficient solar control are necessary.

Technical Specifications

Şişecam Solar Control Low-E Glass Neutral is manufactured by depositing multi-layered metal/metal oxides on float glass through "magnetically enhanced vacuum sputtering" technology.

Performance Tables

Product	Daylight (EN 410)		Solar Energy (EN 410)		Thermal Conductivity (U Value) W / m2K(EN 673)
Product	Transmittance %	Reflectance Outdoor %	Solar Factor %	Shading Coefficient	Argon
4 mm Şişecam Clear Float Glass + 16 mm (cavity) + 4 mm Şişecam Clear Float Glass	82	15	78	0.90	2.6
4 mm Şişecam Solar Control Low-E Glass Neutral + 16 mm (cavity) + 4 mm Şişecam Clear Float Glass	66	25	44	0.50	1.1
(4+0.76+4) mm Şişecam Laminated Solar Control Low-E Glass Neutral + 16 mm (cavity) + 4 mm Şişecam Clear Float Glass	64	24	40	0.47	1.1
4 mm Şişecam Solar Control Low-E Glass Neutral + 16 mm (cavity) + 4 mm Şişecam Clear Float Glass(*) + 16 mm (cavity) + 4 mm Şişecam Low-E Glass	58	27	39	0.45	0.6
6 mm Şişecam Solar Control Low-E Glass Neutral 62/44 + 16 mm cavity + 6 mm Şişecam Clear Float Glass	63	23	43	0.49	1.1
6 mm Şişecam Solar Control Low-E Glass Neutral 50/33 + 16 mm cavity + 6 mm Şişecam Clear Float Glass	49	31	33	0.37	1.1

Şişecam Glass performances are calculated with WinSLT.

“Daylight” and “Solar Energy” properties are calculated using spectral measurements in compliance with EN 410:2011.

“U-value” is calculated according to EN 673:2011. The emissivity measurements used for calculations are in compliance with EN 673:2011 (Annex A) and EN 12898:2019.

Thermal stresses or building codes may require the use of heat-treated glass. This document is not an evaluation of the risk of glass breakage from thermal stresses. Please contact Şişecam Flat Glass to ensure the correct form of glass to be supplied for the structure.

Şişecam Flat Glass cannot be held responsible for any deviations between the presented data and the conditions on the site. This document is for informational purposes only. Technical and other data are based on information available at the time of preparation of this document and are subject to change by Şişecam Flat Glass without notice.

Daylight Transmittance (%): The ratio of the visible spectrum (light) that is transmitted through glass.
Daylight Reflectance (outdoor) (%): The ratio of the visible spectrum (light) that is reflected outside by glass.
Solar Factor: The percentage of total solar radiant heat energy entering the room thorough the glass. The lower solar factor means better solar control.
Shading Coefficient: The ratio of solar factor of a particular glass type to the solar factor of 3 mm clear float glass, set in identical conditions. The lower shading coefficient means better solar control.
U value (W/m2K): A measure of the rate of heat loss of a building component. The lower U value means better heat control and more comfort in winter.

Thickness and Sizes

Thickness (mm)	Standard Sizes (mm)
4,0	3210x2250
	3210x2550
	3210x6000
6,0	3210x2250
	3210x2550
	3210x6000

The tolerances on nominal sizes are ± 5 mm. In addition to above data, other thickness and sizes can be applied. For more information, please ask for Şişecam Flat Glass.

Processing

Particular care should be taken for transporting, storing, cutting and washing of Şişecam Solar Control Low-E Glass Neutral.
Şişecam Solar Control Low-E Glass Neutral is affected by acid. Since human perspiration is acidic, care must be taken so that the coating is not damaged by fingerprints. Wearing clean and waterproof gloves is therefore absolutely essential when manipulating coated glass. Dirty and oily gloves should be changed immediately. They can be used again after truly washing and drying.
During the cutting process of coated glass, care should be taken that the uncoated side of the glass is placed downwards to the cutting table. It is always the coated side that is scored. Suction cups should be applied to the uncoated surface when placing the glass to the cutting table. Manual cutting is not recommended for soft Şişecam Solar Control Low-E Glass Neutral. For machine cutting, highly volatile cutting oil must be used.
Before insulating glass unit production Solar Control Low-E coating must be removed 10 mm from the edges of the Şişecam Solar Control Low-E Glass Neutral.
Şişecam Solar Control Low-E Glass Neutral should be washed with soft bristle brushes and demineralized water with a conductance not exceeding 30 µs/cm should be used.
Cut size Solar Control Low-E coated glass panes must not be left out unpacked. All processes from cutting through to insulating glass unit assembly must be completed in the same day.
Solar Control Low-E coating can be placed on the 2nd surface of the insulating glass unit.
Provided the below instructions are followed, the storage time for a sealed stack of Solar Control Low-E coated glass is 6 months.
- Şişecam Solar Control Low-E Glass Neutral packs must not be uncovered until the temperature of the pack and that of each individual glass pane has reached to equilibrium with the temperature of the processing hall. (Opening stacks or packs before achieving the production hall temperatures, may entail condensation of humidity in between the individual panes with adverse effects on the coating).
- Condensation may be observed on the outer surface of the first and last glass panes. While unpacking, there is a possibility of water droplets to get between the glass panes In order to avoid this situation corresponding glass panes should be dried properly.
- Also the packaging material of glass packs and stacks should not be removed until the cutting process.
- The temperature of the plant area should not fall below 15°C. Storage in the vicinity of doors must be avoided.
- The plant, production hall and transportation areas should be free of aggressive fumes. (Particular care should be taken that the hydrochloric acid etc. substances should not be stored at the same area.)
- After the surrounding tape of the Şişecam Solar Control Low-E Glass Neutral has been removed, any remains of dehumidifying agent must be removed from the upper edge of the stack or pack. Any dehumidifying agent remaining on the upper edge of the glass will produce scratches when it enters into the space between the panes on handling of the individual sheets. Residue on the uncoated side by the surrounding tape can be cleaned by mild agents and ethyl alcohol.
- Remaining pieces or lites of the Şişecam Solar Control Low-E Glass Neutral should be re-sealed using the same packing materials, renewing the dehumidifying agent. Before packaging operation, the color of the randomly chosen dehumidifying agent should be checked. In case the color of the dehumidifying agent is pink, then it should be changed.

Downloads

Coated Glass Performances Coated Glass Brochure